From design to production. We provide feasibility analyses, market research and trial launch for each injection mold. We are committed to helping customers win the market in a real sense, rather than simply OEM plastic production. We will customize at least 3 solutions and offer you a $500 discount on your first mold.
Confidentiality Agreement | Collaborative Office Systems | Videoconferencing | Fabrication in China | Win of the market | A stable supply
ABS D-190 Physical Properties Data Sheet
Performance of the project |
Test conditions |
Test method |
Value/Description |
Unit |
|
Mechanical properties | Tensile strength (tensile strength) | ASTM D638/IS0 527 | 500 (7,090) | kg/cm2(MPa)[Lb/in2] | |
Elongation at break | ASTM D638/IS0 527 | % | |||
The tensile modulus | ASTM D638/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
Tensile yield elongation (elongation) | ASTM D638/ISO 527 | 15 | % | ||
Elongation at break of tensile tenancy | ASTM D638/IS0 527 | % | |||
Bending modulus (bending elasticity) | ASTM D79O/ISO 178 | 25000 (35000) | kg/cm2(MPa)[Lb/in2] | ||
The bending strength | ASTM D790/ISO 178 | 790(11,660) | kg/cnr (MPa)[Lb/in2] | ||
Rockwell hardness | ASTM D785 | R-105 | |||
IZ0D Notch Impact Strength | 1/4" 23℃ | ASTM D256/ISO 179 | kg • cm/cm(J/M) ft • lb/in | ||
1/4" -30℃ | ASTM D256/IS0 179 | 14(2.6) | kg • cm/cm(J/M) ft • lb/in | ||
1/8" 23℃ | ASTM D256/ISO 179 | kg • cm/cm(J/M) ft • lb/in | |||
1/8" -30℃ | ASTM D256/ISO 179 | 15(2.7) | kg • cm/cm(J/M) ft • lb/in | ||
Charpy Impact Strength | 23℃(gap) | ASTM D256/ISO 179 | kg • cm/cm(J/M) ft • lb/in | ||
-30℃(gap) | ASTM D256/ISO 179 | kg • cm/cm(J/M) ft • lb/in | |||
23℃ (no gap) | ASTM D256/ISO 179 | kg • cm/cm(J/M) ft • lb/in | |||
-30℃ (no gap) | ASTM D256/ISO 179 | kg • cm/cm(J/M) ft • lb/in | |||
Physical properties | Specific gravity (density) | ASTM D792/ISO 1183 | 1.05 | ||
Molding shrinkage | ASTM D955 | % | |||
Melt index (flow coefficient) | 200℃/5kg | ASTM D1238/ISO 1133 | 1.9 | g/10min | |
220℃/10kg | ASTM D1238/ISO 1133 | 23 | g/10min | ||
Thermal performance | Thermal Deformation Temperature | annealing | ASTM D648/IS0 75 | 99(210) | ℃(℉) |
Without annealing | ASTM D648/ISO 75 | 88(190) | ℃(℉) | ||
Veka softening point | ASTM D1525/IOS R306 | ℃(℉) | |||
Melting Point | - | ℃(℉) | |||
Flammability (Rate) | UL94 | 1/16"HB | |||
Linear Coefficient of Expansion | ASTM D696/ISO 11359 | mm/mm℃ | |||
Processing conditions | Dry conditions | ||||
Processing Temperature | nozzle | ℃ | |||
Cylinder recently | ℃ | ||||
Cylinder in the middle | ℃ | ||||
After the cylinder | ℃ | ||||
Melt Temperature | ℃ | ||||
Melt Temperature | ℃ | ||||
Melt Temperature | Injection pressure | Mpa | |||
Holding Pressure | Mpa | ||||
Back pressure | Mpa | ||||
Screw Rotation Speed | rpm | ||||
Other | Note | ||||
Color | |||||
Features | High rigidity medium impact | ||||
Use |
ABS HJ-15A Physical Property Table Parameters | ||||
Product introduction | Applied to electronic appliances and building materials. | |||
Performance | Test Conditions | Unit | Test Method | Numerical |
Density | g/cm³ | ASTM D792 | 1.05 | |
Melt Volume Flow | 200°C/10.0 kg | cm³/10min | Internal methods | 21 |
Notched impact strength of simply supported beams | -23°C | kJ/m² | ISO179 | 62 |
Tensile Modulus | -30°C | MPa | ASTM D638 | 2750 |
Veka Softening Temperature | Thickness 1.50mm | °C | Rate B; ASTM D1525 | 103 |
Combustible (UL94) | 1.30mm | class | IEC 60695-11-10 | HB |
ABS HJ-15A The following parameters should be noted during injection molding | |
Injection | Rating(System of units) |
Drying temperature | 80.0~85.0°C |
Drying time | 2.0~4.0hr |
Recommended Maximum Moisture Content | 0.020% |
Temperature of the Hopper | 60.0~80.0°C |
Rear Temperature of Barrel | 180~220°C |
Middle tTemperature of Barrel | 190~230°C |
Front Temperature of Barrel | 190~ 230°C |
Nozzle Temperature | 185~235°C |
Processing (Melt) Temperature | 190~ 230°C |
Mold Temperature | 30.0~ 70.0°C |
Vent Depth | 0.030~0.075mm |